BEND TESTS


BEND TESTS

Object: 

To determine the soundness of weld metal, heat affected zone and weld zone.These tests may also be used to give some measure of the ductility of the weld zone. It is not usual to use transverse and longitudinal bend tests for the same application.

Method: 

All specimens to be removed and prepared without causing significant distortion or heating. The cap and root are ground flush. The specimen is bent by the movement of a former of prescribed diameter, the relevant side of the specimen to be placed in tension. Angle of bend and diameter of former should be as specified in the appropriate standard.

Reporting Results:
  • Thickness of specimen
  • Direction of bend (root or face)
  • Angle of bend
  • Diameter of former
  • Appearance of joint after bending e.g. type and location of flaws



Labels

Labels:

Popular posts from this blog

The Brinell Hardness Test

The Brinell Hardness Test The Brinell hardness test method consists of indenting the test material with a 10 mm diameter hardened steel or carbide ball subjected to a load of 3000 kg. For softer materials the load can be reduced to 1500 kg or 500 kg to avoid excessive indentation. The full load is normally applied for 10 to 15 seconds in the case of iron and steel and for at least 30 seconds in the case of other metals. The diameter of the indentation left in the test material is measured with a low powered microscope. The Brinell harness number is calculated by dividing the load applied by the surface area of the indentation. The diameter of the impression is the average of two readings at right angles and the use of a Brinell hardness number table can simplify the determination of the Brinell hardness. A well structured Brinell hardness number reveals the test conditions, and looks like this, "75 HB 10/500/30" which means that a Brinell Hardness of 75 was obtained us...
Read more

Part -3 Most commonly asked Mechanical Interview Questions

Most commonly asked Mechanical Interview Questions with answer 1. What is the difference between Technology and Engineering? Ans. Engineering is application of science. Technology shows various methods of Engineering. A bridge can be made by using beams to bear the load,by an arc or by hanging in a cable; all shows different technology but comes under civil engineering and science applied is laws of force/load distribution. 2. How to Measure Temperature in Wet Bulb Thermometer? Ans. Wet bulb temperature is measured in a wet bulb thermometer by covering the bulb with a wick and wetting it with water. It corresponds to the dew point temperature and relative humidity. 3. What are the Advantages and Disadvantages of using LPG in Car? Ans. Advantages 1. Complete combustion 2. Fuel saving 3. Homogenous combustion Disadvantages 1. As complete combustion is occurring ,more heat liberated,not advised for long journey, engine will be over heated 2. In...
Read more

CHARPY V NOTCH IMPACT TEST

CHARPY V NOTCH IMPACT TEST Object : To determine the amount of energy absorbed in fracturing a standardized test piece at a specified temperature. Method : A machined, notched specimen is broken by one blow from a pendulum. Because scatter occurs in the results, at least three specimens are used to assess the joint represented. Testing is carried out at a temperature specified in the appropriate application standard. Reporting Results: Location and orientation of the notch.  Testing temperature. Energy absorbed in joules.  Description of fracture appearance. Location of any defects. The Charpy impact test, measured in joules, is an assessment of TOUGHNESS. Transition temperature (curve) in steel.
Read more